Harvest Technologies

MATERIALS

MATERIALS MATRIX

Material	Process	Part Density (ASTM D792)	Tensile Strength, Ultimate (ASTM D638)	Tensile Modulus (ASTM D638)	Elongation at Break (ASTM D638)	Flexural Strength, Ultimate (ASTM D790)	Flexural Modulus (ASTM D790)	Impact Strength (notched Izod, 23C)	Heat Deflection Temperature (HDT) (ASTM D648@ 1.82 MPa)

Accura 25	Stereolithography	1.19 g/cm³	38 MPa	1,590 MPa	13%	55 MPa	1,380 MPa	19 J/m	51 C
Flex TPE	Laser Sintering	1.03g/cm³	1.8 MPa	7.4 MPa	110%		13 MPa
NanoTool	Stereolithography		61.7 MPa	11,000 MPa	0.7%	79 MPa	10,200 MPa	.001 J/m	85 C
NeXt	Stereolithography		31 MPa	2,370 MPa	8%	67.8 MPa	2,415 MPa	.005 J/m	48 C
Nylon CG	Laser Sintering	.84g/cm³	48 MPa	3,378 MPa	4%
Nylon D80	Laser Sintering	1.04g/cm³	35 MPa	1,392 MPa	32%		868 MPa	69 J/m	43 C
Nylon EX	Laser Sintering	1.01>g/cm³	48 MPa	1,517 MPa	47%	46 MPa	1,310 MPa	74 J/m	48 C
Nylon FR-106	Laser Sintering	1.07g/cm³	46 MPa	1,392 MPa	38%		1,345 MPa	69 J/m	70 C
Nylon GF	Laser Sintering	1.49g/cm³	26 MPa	4,068 MPa	1.4%	37 MPa	3,106 MPa	41 J/m	134 C
Nylon HST	Laser Sintering	1.20g/cm³	51 MPa	5,725 MPa	4.5%	89 MPa	4,550 MPa	37.4 J/m	179 C
Nylon PA	Laser Sintering	1.02g/cm³	48 MPa	1,700 MPa	24%		1,500 MPa	220 J/m	86 C
ProtoGen O-XT 18420	Stereolithography	1.18 g/cm³	42.2 MPa		8%	66.7 MPa	1,990 MPa	.002 J/m	46 C
ProtoTherm 12120	Stereolithography	1.17 g/cm³	77 MPa	3,250 MPa	04.5%	103 MPa	3,060 MPa	.001 J/m	110 C
RenShape 7820	Stereolithography	1.13 g/cm³	36 MPa	1,900 MPa	8%	59 MPa	2000 MPa	42 J/m	51 C
WaterShed XC 11122	Stereolithography	1.14 g/cm³	47.1 MPa	2,650 MPa	11%	63 MPa	1,040 MPa	0.002 J/m	49 C